Waterborne polyurethane resin (aliphatic)

Product Code
Solid Content (%)
Co-Solvent
Co-Solvent(%)
Product Features
TDS
MSDS
PU 147
0051
NEP
4
PU 147 is an anionic aliphatic waterborne polyurethane dispersion. It has good weather resistance, high gloss, high temperature and humidity resistance, and non-stickiness. It feels soft and toughness.
PU 150
0051
Acetone
˂̳0.1
PU 150 is an anionic aliphatic waterborne polyurethane dispersion. it has high tensile strength, soft feel, and good toughness, and is resistant to low-temperature bendability.
PU 153
0051
Acetone
˂̳0.1
PU 153 is an anionic aliphatic waterborne polyurethane dispersion. It has high tensile strength and good anti-sticking.
PU 161
35±1
Acetone
˂̳0.1
PU 161 has excellent adhesion and high strength. Suitable for leather finishing, textile, PVC film, adhesives, etc.
PU 273
0051
Acetone
˂̳0.1
PU 273 is an anionic aliphatic waterborne polyurethane dispersion.
PU 276
1051
Acetone
˂̳0.1
PU 276 is an anionic aliphatic waterborne polyurethane dispersion. It builds soft and smooth with high fullness film. It has excellent water resistance and low-temperature resistance.
PU 277
1051
Acetone
˂̳0.1
PU 277 It builds soft and smooth with high fullness film. It has excellent water resistance and low-temperature resistance.
PU 278
1051
Acetone
˂̳0.1
PU 278 It builds soft and smooth with high fullness film. It has excellent water resistance and low-temperature resistance.
PU 279
1051
Acetone
˂̳0.1
PU 279 It builds soft and smooth with high fullness film. It has excellent water resistance and low-temperature resistance.
PU 311
35±1
Acetone
˂̳0.1
PU 311 is an anionic aromatic waterborne polyurethane dispersion. It has excellent water resistance, resistance to low temperature and twists, soft hand feeling and good elasticity. Suitable for leather finishing, textile coatings, adhesives, etc.
PU 335
35±1
Acetone
˂̳0.1
PU 335 is an anionic aromatic waterborne polyurethane dispersion. The product has good elasticity and soft hand feeling and strong adhesion. Suitable for leather finishing, textile coatings, adhesives, etc.
PU 390
35±1
Acetone
˂̳0.1
PU 390 is an anionic aromatic waterborne polyurethane dispersion. The product has good resistance to back-sticking, bottom odor, low VOC, no APEONMP and tin substances. Suitable for leather coating, PVC film, textile, etc.
PU 398
38±1
Acetone
˂̳0.1
PU 398 is an anionic aromatic waterborne polyurethane dispersion. The product has high tensile strength, good resistance to back-adhesion, and is suitable for leather coating, PVC film, textiles, etc.
PU 610
35±1
Acetone
˂̳0.1
PU 610 is an anionic aliphatic waterborne polyurethane dispersion with high hardness, high gloss and high tensile strength. Has excellent adhesion. Mainly used for leather finishing, PVC film, PET film, textile coating, etc.
PU 6260
0051
Acetone
˂̳0.1
PU 6260 is an anionic aliphatic waterborne polyurethane dispersion. This product has high tensile strength, soft hand feeling and good toughness. Mainly used for leather finishing, VC film, PET film, textile coating, etc.
PU 6263
0051
Acetone
˂̳0.1
PU 6263 is an anionic aliphatic waterborne polyurethane dispersion. This product has high tensile strength and smooth hand feeling. Suitable for leather finishing, VC film, PET film, textile coating, etc.
PU 6266
0051
Acetone
˂̳0.1
PU 6266 is an anionic aliphatic waterborne polyurethane dispersion. The product has excellent water resistance, good weather resistance, soft hand feeling and good toughness. Suitable for leather finishing, adhesives, textile coatings, etc.
PU 630
35±1
Acetone
˂̳0.1
PU 630 is an anionic aliphatic waterborne polyurethane dispersion. The product feels smooth and elastic, has good adhesiveness, scratch resistance and solvent resistance. Mainly used for leather finishing, PVC film, PET film, wood coatings, etc.
PU 631
0051
Acetone
˂̳0.1
PU 631 is an anionic aliphatic waterborne polyurethane dispersion.
WELLPUR FF 18D
30±1
DMM
5
WELLPUR FF 18D is a formaldehyde-free cationic aliphatic polyurethane dispersion. It has excellent adhesion on various substrates. It can be used as a bridging agent and mixed with various dispersions to form a transparent, flexible and slightly sticky film.
WELLPUR FM 14A
0051
NEP
4
WELLPUR FM 14A is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhersion. It is suituable in leather application.
WELLPUR FM 15A
30±1
NEP
4
WELLPUR FM 15A is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhersion. It is suituable in leather application.
WELLPUR PU 8501F
7251
\
\
WELLPUR PU 8501F is an aqueous dispersion of polyether polyurethane without any organic solvents. After the product is formed into a film, it is naturally dull and has an obvious "soft rubber touch".
WELLPUR RM 14A
0051
NEP
4
WELLPUR RM 14A is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhersion. It is suituable in leather application.
WELLPUR RM 23NI/P
30±1
NEP
4
WELLPUR RM 23NI/P is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhersion. It is suituable in leather application.
WELLPUR RM 249A
0051
NEP
4
WELLPUR RM 249A is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhersion. It is suituable in leather application.
WELLPUR RM24
35±1
NEP
4
WELLPUR RM 24 is an aliphatic waterborne polyurethane dispersion, it has soft feel, and excellent adhesion. It is suitable in leather application.
WELLPUR TR32
35±1
NEP
4
WELLPUR TR 32 is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhesion. It is suitable in leather application.
WELLPUR TR435
35±1
NEP
4
WELLPUR TR 435 is an aliphatic waterborne polyurethane dispersion, it It has soft feel, and excellent adhesion. It is suitable in leather application.
PU 162
35±1
Acetone
<0.5
Anionic aliphatic waterborne polyurethane dispersion. It has good compatibility with various types of waterborne polyurethane dispersions and acrylic emulsions.
P-511
20%±0.5
/
Apply in colorful paints, as an isolating agent to separate colors.

Waterborne arcylic resin

Product Code
Solid Content (%)
Co-Solvent
Co-Solvent(%)
Product Features
TDS
MSDS
PA1001
0251
ammonia
˂̳0.1
PA1001 (acrylic light soft) is an anionic styrene-acrylic emulsion. The product adopts the self-crosslinking technology at room temperature, the film-forming drying speed is fast, and it is easy to polish. Has excellent thixotropy and adhesion.
PA1002
0251
ammonia
˂̳0.1
PA1002 (acrylic light hard) is an anionic styrene-acrylic emulsion. It has excellent compatibility with various types of waterborne polyurethane dispersions and acrylic emulsions.
PA1003
1052
ammonia
˂̳0.1
PA1003 is an anionic styrene-acrylic emulsion. The product adopts normal temperature self-crosslinking technology, and the film is soft and tough. It has excellent compatibility with various types of waterborne polyurethane dispersions and acrylic emulsions.
PA1004
1052
ammonia
˂̳0.1
PA1004 is an anionic styrene-acrylic emulsion. The product adopts normal temperature self-crosslinking technology, and the film is soft and tough. It has excellent compatibility with various types of waterborne polyurethane dispersions and acrylic emulsions.
PA2001
45±1
ammonia
˂̳0.1
PA2001 is an anionic pure acrylic emulsion. The product has fast film-forming drying speed, easy sanding, and good thickening response. It has excellent compatibility with various types of waterborne polyurethane dispersions and acrylic emulsions.
PA2002
45±1
ammonia
˂̳0.1
PA2002 is an anionic pure acrylic emulsion. The product has fast film-forming drying speed, easy sanding, and good thickening response. It has excellent compatibility with various types of waterborne polyurethane dispersions and acrylic emulsions.

Hardener

Product Code
Solid Content (%)
Co-Solvent
Co-Solvent(%)
Product Features
TDS
MSDS
TC Linker 30
30
Water
69-70
TC Linker 30 is a polymerizable aliphatic pure water-based crosslinking agent, which does not contain VOC and has a solid content of 30%. Used as an environmentally friendly crosslinking agent for aqueous polymer dispersions, such as polyurethane and acrylic emulsions containing carboxyl groups.
TC Linker 60
60
DPM
39-40
TC Linker 60 is a polymerizable aliphatic crosslinking agent with DPM (dipropylene glycol methyl ether) as a carrier. It can be used as a crosslinking agent for polymers containing carboxyl groups, such as polyurethane and acrylic resins containing carboxyl groups.
TC Linker 70
70
/
/
TC Linker 70 is a hydrophilic aliphatic polyisocyanate type crosslinking agent based on hexamethylene isocyanate. Due to its hydrophilicity, it can easily be added in water or in aqueous solutions containing polymer dispersions.

Wax emulsion

Product Code
Solid Content (%)
Co-Solvent
Co-Solvent(%)
Product Features
TDS
MSDS
WAX-100
30
/
/
Polishable matt black wax: does not turn white before dry film polishing, high transparency, high oiliness and high brightness.
WAX-101
35
/
/
It does not contain emulsifiers, it is anti-sticking, slippery, wear-resistant, and has good water resistance.
WAX-200
25
/
/
Non-ionic Fischer-Tropsch wax microemulsion, high gloss, brighter after polishing. Compared with PE wax and carnauba wax, the wax has a special slippery feel.
WAX-201
25
/
/
Non-ionic Fischer-Tropsch wax dispersion. It is a polishable matte black wax dry film without whitening before polishing, high matteness, high transparency, high oiliness, high brightness and high blackness after polishing. Compar with Polyethylene wax emulsion, it has easier polishing, better hand feel, more natural visual gloss, and lower friction coefficient.
WAX-300
40
/
/
High density oxidized polyethylene wax microemulsion. The most classic high-density curing polyethylene wax emulsion formula. The main purpose is polishing and wear resistance. It has a tendency to pulverize after drying, and is generally used in conjunction with water-based resins. Due to the high molecular weight chemical structure, it has a strong affinity for PE, PP, etc. It can be used for all kinds of paper-plastic laminating adhesives and has the strongest paper-PE adhesion.
WAX-400
35
/
/
High density oxidized polyethylene wax microemulsion. The most classic high-density curing polyethylene wax emulsion formula. The main purpose is polishing and wear resistance. It has a tendency to pulverize after drying, and is generally used in conjunction with water-based resins. Due to the high molecular weight chemical structure, it has a strong affinity for PE, PP, etc. It can be used for all kinds of paper-plastic laminating adhesives and has the strongest paper-PE adhesion.
TCS3010
Natural Gloss
The gloss is natural, the grain surface is clear, the wax feels good
TCS3310
Medium Gloss
The film is weak, the wax feel is good, can be used for shoe milk spraying, adaptability is wide.
TCS3050
Medium High Gloss
Film-forming medium, high-gloss, waxy, grainy clear
TCS3060
High Gloss
Film forming slightly stronger, good adhesion, high gloss
TCS5010
Matt
Full matte, fast dry, waxy, full of grain
TCS5030
Medium Gloss
Bright light, good wax, full grain
TCS5020
Medium High Gloss
Medium wax oil, wax feel good, grain surface clear
TCS5080
High Gloss
Highlights, good wax, cost-effective
TCS5110
The gloss is natural and the wax feels good
R88 series
Good coloring, grain surface clear, natural gloss, easy to operate
S66 series
Good coloring, strong wax, strong oily feeling
Series Y
Low odor, good color display, high color concentration, cost-effective
TCS5000
Matte, oily feel good
TCS5120
Medium gloss, good wax
TCS5130
It feels smooth and waxy
TCS5310
The smell is fragrant, the paste is delicate and exquisite, the wax feels good, the grain surface is clear
TCS5320
Wax feels good and the grain is clear
TCS5800
High gloss, good paste consistency, strong operability
TCS8100
Wax is soft and delicate, and has good filling
TCS8110
Wax feel strong, good filling, easy to wax
TCS8200
Easy to burn
TCS8300
High gloss, strong wax, easy to polish
TCS8500
The leather fades well
TCS9000
Coloring force and color display is good, waxy, rich in color